UNS N04400 DIN 17750 Monel 400 BS 3076NA13 BS 3072NA1 plate sheet
1.Monel 400® Sheet/Plate Specifications
| UNS: | N04400 |
| Specifications: | ASTM B127, AMS 4544 |
| International Specifications: | BS 3072NA1, BS 3073NA13, QQ-N-281, DIN 17750 |
2.What is Monel Alloy 400 Sheet & Plate
Monel 400 Sheet & Plate is a copper-nickel base alloy plate. Along with these, it is traced with the amount of manganese, silicon, and carbon content. These alloy 400 plates have good ductility and facilitate superior resistance to a broad range of corrosive circumstances. These plates exhibit outstanding resistance to alkaline and acidic environment. However, it posses great thermal conductivity in annealed conditions. This grade of plates comprises high tensile strength and toughness. Furthermore, these are suitable in subzero temperature from 1000 °F. Thus these plates get good hardness by the cold working process.
The model 400 plates and sheets resist stress corrosion cracking and pitting corrosion. Therefore it shows good resistance to marine conditions. however, these are designed in the cold and hot rolled formed.
As the reputed firm in the market, Rexton Steel & Alloys provides a wide collection of Monel 400 Sheet & Plate. Therefore we manufacture and supply product to our domestic as well as global clients at cost effective rate.
3.400 Monel Sheets & Plates– Equivalent Grades
| STANDARD | WERKSTOFF NR. | UNS | JIS | BS | GOST | AFNOR | EN |
| Monel 400 | 2.4360 | N04400 | NW 4400 | NA 13 | МНЖМц 28-2,5-1,5 | NU-30M | NiCu30Fe |
4.Monel 400 Sheets & Plates Chemical Composition
| Grade | C | Mn | Si | S | Cu | Fe | Ni |
| Monel 400 | 0.30 max | 2.00 max | 0.50 max | 0.024 max | 28.00 – 34.00 | 2.50 max | 63.00 min |
| Element | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| Monel 400 | 8.8 g/cm3 | 1350 °C (2460 °F) | Psi – 80,000 , MPa – 550 | Psi – 35,000 , MPa – 240 | 40 % |
........................................................................